No. | La profundidad o.w.f % | C.I.No. | La solidez del teñido | ||||||
La luz (Xenon) | Lavado | La transpiración | Frota | ||||||
Nombre de tintes | Muestra de color del algodón | 40º C. | 60°C. | ||||||
CH/CO/V. | CH/CO/V. | CH/CO/V. | Dry/Wet | ||||||
1 | Mezcla directa brillante D-GL | 1.0 | - | 4 |
4
4-5 4 |
4-5
3-4 4-5 |
4-5
3-4 4-5 |
4-5
3-4 |
|
2 | Mezcla directa amarillo D-2RL | 1.0 | 5 |
3-4
4 4-5 |
3-4
4 4 |
3
4-5 4-5 |
4-5
3 |
||
3 | Mezcla directa amarillo D-3RNL | 1.0 | 161 | 4 |
3-4
4-5 4-5 |
3-4
4-5 4 |
3-4
4-5 4-5 |
4-5
4 |
|
4 | Mezcla directa amarillo D-ARL | 1.0 | 106 | 5-6 |
4-5
4-5 4-5 |
4-5
4-5 4-5 |
4-5
4-5 4-5 |
4-5
4-5 |
|
5 | Mezcla directa Orange D-2GL | 1.0 | 39 | 5 |
-
- - |
3-4
2-3 3 |
4-5
5 4-5 |
4-5
3-4 |
|
6 | Mezcla directa Orange D-5R | 1.0 | - | 3-4 |
4
4 4 |
3-4
4-5 4-5 |
3-4
4-5 4-5 |
3-4
3 |
|
7 | Mezcla directa Scarlet D-GLN | 2.0 | - | 3 |
4-5
4-5 4-5 |
4-5
4 2-3 |
3-4
4-5 4-5 |
4
3 |
|
8 | Mezcla directa Scarlet D-F2G | 2.0 | 224 | 4 |
4
3 4 |
4
3 3 |
4
4 4 |
4
3 |
|
9 | Mezcla directa rojo brillante D-P. | 2.0 | 227 | 3-4 |
4
3 4 |
4
2 2-3 |
3-4
4-5 4-5 |
4-5
3-4 |
|
10 | Mezcla directa Rubine D-BLL | 2.0 | 83:1 | 5-6 |
3-4
4 4-5 |
3
4 4-5 |
3-4
4-5 4-5 |
3
2-3 |
|
11 | Violeta mezcla directa D-5BL. | 2.0 | 66 | 4-5 |
3-4
4-5 4-5 |
4
4 4 |
3-4
4-5 4-5 |
4-5
3-4 |
|
12 | Mezcla directa azul turquesa D-BGL | 2.0 | - | 4 |
4-5
4-5 4-5 |
4-5
4-5 4-5 |
4-5
4-5 4-5 |
4-5
5 |
|
13 | Mezcla directa de Blue D-3GL | 2.0 | 274 | 4-5 |
4-5
4-5 4 |
4-5
4 4 |
4
4-5 4-5 |
4-5
4-5 |
|
14 | Mezcla directa de Blue D-RGL | 2.0 | 70 | 4-5 |
3-4
4-5 4-5 |
3-4
3-4 4-5 |
3-4
4-5 4-5 |
4
2-3 |
|
15 | Mezcla directa de Marina D-R | 2.0 | 297 | 3-4 |
4-5
4 4-5 |
-
- - |
4-5
4-5 4-5 |
4-5
2-3 |
|
16 | Mezcla directa Brown D-RS. | 2.0 | - | 3 |
3-4
4 4-5 |
3
4 4-5 |
3-4
4 4-5 |
4-5
4 |
|
17 | Gris mezcla directa D-B | 2.0 | - | 3-4 |
3-4
3-4 4-5 |
4-5
3 3-4 |
4-5
4-5 4-5 |
4-5
3-4 |
|
18 | Negro mezcla directa D-RR.HH. | 5.0 | 173 | 3-4 |
3-4
4-5 4-5 |
3-4
4 4 |
4
4-5 4-5 |
3
2 |
|
19 | Negro mezcla directa D-RSN | 5.0 | - | 3-4 |
3-4
4-5 4-5 |
-
- - |
3
4-5 4-5 |
4
3 |
|
20 | Negro mezcla directa D-OB | 5.0 | 80 | 3 | 3-4 |
-
- - |
-
- - |
-
- |