| La Chine | Le Japon | U.S. | L'Allemagne | La dureté |
| L'OCr18NI9 | SUS304 | L'AISI304 | 1.4301 | HRC 25-39 |
| 00Cr19Ni10 | SUS304L | L'AISI304L | 1.4307 | HRC 25-39 |
| 0CR17Ni12Mo2 | SUS316 | AISI316 | 1.4401 | HRC 25-39 |
| 0CR19Ni12Mo2 | SUS316L | L'AISI316L | 1.4404 | HRC 25-39 |
| 3Cr13 | 420J2 | L'AISI420 | 1.4028 | HRC 48-58 |
| 4Cr13 | - | L'AISI420C | 1.3541, 1.4034 | HRC52-56 |
| 9Cr18 | - | L'AISI440 | HRC57-61 | |
| 9CR18Mo | SUS440C | L'AISI440C | 1.4125 | HRC58-64 |
| Matériel | La composition chimique % | ||||||||
| C | Si | Mn | P | S | Ni | Cr | Mo | Ti | |
| L'AISI304 | ≤0,08 | ≤1,00 | ≤2,00 | ≤0,045 | ≤0,03 | 8.0-11.0 | 18-20 | ||
| L'AISI304L | ≤0,03 | ≤1,0 | ≤2,00 | ≤0,045 | ≤0,03 | 9.0-12.0 | 18-20 | ||
| AISI316 | ≤0,08 | ≤1,00 | ≤2,00 | ≤0,035 | ≤0,03 | 10.0-14 | 16.0-18.5 | 2.0-3.0 | |
| L'AISI316L | ≤0,030 | ≤1,00 | ≤2,00 | ≤0,045 | ≤0,03 | 10.0-14 | 16.0-18 | 2.0-3.0 | |
| L'AISI420(3Cr13) | 0.26-0.35 | ≤1,0 | ≤1,0 | ≤0,04 | ≤0,035 | ≤≤ 0,60 % | 12.0-14.0 | ||
| L'AISI420C(4Cr13) | 0.36-0.45 | ≤0,60 | ≤0,8 | ≤0,035 | ≤0,03 | ≤0,6 | 12.0-14.0 | ||
| L'AISI440 (9Cr18) | 0,9-1 | ≤0,8 | ≤0,8 | ≤0,035 | ≤0,80 | ≤0,60 | 17.0-19.0 | ≤0,75 | |
| L'AISI440C (9Cr18Mo) | 0,9-1 | ≤0,8 | ≤0,8 | ≤0,035 | ≤0,03 | ≤0,60 | 16.0-18.0 | ≤0,75 | |
| Grade : G10 à G1000 | |||||
| Grade | Diamètre de balle | Sphérique | Surface | Beaucoup de diamètre | Bille nomainal |
| La variation | Déviation | La rugosité | La variation | La tolérance déviation | |
| Vdws | Sph | Ra | Vdwl | Tdn | |
| Pas plus de | |||||
| Μm | |||||
| 10 | 0.25 | 0.25 | 0.02 | 0,5 | * |
| 16 | 0,4 | 0,4 | 0,025 | 0,8 | * |
| 20 | 0,5 | 0,5 | 0,032 | 1 | * |
| 24 | 0,6 | 0,6 | 0.04 | 1.2 | * |
| 28 | 0,7 | 0,7 | 0,05 | 1.4 | * |
| 40 | 1 | 1 | 0.06 | 2 | * |
| 60 | 1.5 | 1.5 | 0.08 | 3 | * |
| 100 | 2.5 | 2.5 | 0,1 | 5 | ±12,5 |
| 200 | 5 | 5 | 0.15 | 10 | ±25 |
| 500 | 12.5 | 12.5 | * | 25 | ±50 |
| 1000 | 25 | 25 | * | 50 | ± 125 |