Aluminium A96110 and Aluminium Alloy A96110 Sheet or Plate

Model NO.
6110 A/6110-T9/A96110 /AlMg0.9Si0.9MnCu
Surface Treatment
Mill Finish
Alloy
Alloy
Temper-1
6065-0/111/T4/T42/T451/T5/T6/T61/6151/62/651
Melting Point
600-650
Density
2.7-2.8g/cm3
Standard
ASTM B317 /SAE J454
Application-1
Structural Applications Marine Applications Ladder
Form
Sheet,Plate,Bar,Rod,Tube,Pipe,Strip,Foil an
Transport Package
Standard Export Packaging
Specification
0.5-200mm*500-2500mm*500-100000mm
Trademark
Taixie
Origin
China
HS Code
7606910000
Production Capacity
10 Tons Per Month
Reference Price
$ 17.10 - 26.10
Contact Us

Product Description

[aluminium  alloy 6110 /6110-T9/A96110/AlMg0.9Si0.9MnCu] 
Introduction:

6110 aluminum is a 6000-series aluminum alloy: there is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. Cited properties are appropriate for the T9 temper. To achieve this temper, the metal is solution heat-treated, artificially aged, then strain hardened. 6110 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-6110. A96110 is the UNS number.

It originally received its standard designation in 1979.

It has the highest tensile strength among the 6000-series alloys in the database.

The graph bars on the material properties cards below compare 6110 aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

[aluminium  alloy 6110 /6110-T9/A96110/AlMg0.9Si0.9MnCu ] 
Application:


 

[aluminium  alloy   6110 /6110-T9/A96110/AlMg0.9Si0.9MnCu  ] 
Chemistry:


Chemical composition %   of grade   ENAW-AlMg0.9Si0.9MnCu   ( ENAW-6110A )

Fe Si Mn Cr Cu Mg Zn Others -
max   0.5 0.7 - 1.1 0.3 - 0.9 0.05 - 0.25 0.3 - 0.8 0.7 - 1.1 max   0.2 each 0.05; total 0.15 Ti+Zr < 0.2; Al - remainder

Mechanical properties of grade   ENAW-AlMg0.9Si0.9MnCu   ( ENAW-6110A )

Rm  - Tensile strength (MPa) (T5) 380
Rm  - Tensile strength (MPa) (T6) 380-410
Rm  - Tensile strength (MPa) (T4) 320
 
R p0.2  0.2% proof strength (MPa) (T5) 360
R p0.2  0.2% proof strength (MPa) (T6) 360-380
R p0.2  0.2% proof strength (MPa) (T4) 220
 
A  - Min. elongation at fracture (%) (T5) 10
A  - Min. elongation at fracture (%) (T6) 10
A  - Min. elongation at fracture (%) (T4) 16
 
A  - Min. elongation Lo = 50mm (%) (T5) 8
A  - Min. elongation Lo = 50mm (%) (T6) 8
A  - Min. elongation Lo = 50mm (%) (T4) 14
 
  Brinell hardness   (HBW):   (T5) 115
  Brinell hardness   (HBW):   (T6) 120
  Brinell hardness   (HBW):   (T4) 85


Properties ENAW-AlMg0.9Si0.9MnCu
Intended to be contact with food - no;
 

[aluminium  alloy   6110 /6110-T9/A96110 /AlMg0.9Si0.9MnCu   ] 

Surface 

mill finish ,   n ot polished,
brushed
mirror 
embossed 
oxidized
cold-rolled
hot-rolled

[aluminium  alloy    6110 /6110-T9/A96110/AlMg0.9Si0.9MnCu  ]
Specification:

Shape/Form : sheet,plate,bar,rod,tube,pipe,strip,foil and so on 

Surface : Mill Finish(Not Polished ) ,p olished  ,colour-coated , sand blasting  , brushed,mirror ,embossed ,oxidized,anodic oxidation      cold-rolled,hot-rolled   


This  is our  warehouse : Aluminium A96110 and Aluminium Alloy A96110 Sheet or Plate


Aluminium A96110 and Aluminium Alloy A96110 Sheet or Plate



Aluminium A96110 and Aluminium Alloy A96110 Sheet or Plate




This  is packaging :

Aluminium A96110 and Aluminium Alloy A96110 Sheet or Plate



 

 

Aluminum Sheet

TREF.COM.MK, 2023